ZANDER 4009 Fe
Material number
1.4009
EN ISO 3581-A
E 13 B 42
EN 1600
E 13 B 42
AWS A 5.4
E 410-25
Applications / Features
Basic-coated high-performance electrode for hardfacing and joint welds on ferritic-martensitic chromium steels (e.g. 13%Cr steels).
For operating temperatures up to 450°C
Like similar-grade chromium steels, the weld metal is corrosion-resistant.
Preheating of the workpiece to 200°C if the base material does not require a higher preheat.
Applications
Suitable for base materials such as:
1.4000 (X 6 Cr 13),
1.4001 (X 7 Cr 14),
1.4002 (X 6 CrAl 13),
1.4006 (X 12 Cr 13),
1.4021 (X 20 Cr 13),
1.4024 (X 15 Cr 13).
Suitable for sealing surface overlays on:
Gas, water and steam valves/fittings.
Indicative analysis [%]
C
Si
Mn
Cr
Ni
Fe
0,06
0,30
0,50
12,50
0,10
balance
Recovery
150%
Redrying
320°C / 2h
Current type
=(+)
Positions
pa
pb
pc
pf
Properties: (without heat treatment; indicative values at room temperature)
Tensile strength Rm
650 [MPa]
hardness
180 [HB 30]
Yield strength ReH/Rp0,2
450 [MPa]
hardness (ungegluht)
35 [HRC]
Elongation (L=5d)
15 [%]
Dimensions
Ø [mm]
Length [mm]
Welding current [A]
2,5
350
60-90
3,2
350
80-110
4,0
450
100-150
5,0
450
150-200